Title: Efeito do reuso sobre as características de superfície e da composição química de instrumentos de NiTi
???metadata.dc.creator???: Bastos, Mariana Mena Barreto 
???metadata.dc.contributor.advisor1???: Sponchiado Junior, Emílio Carlos
???metadata.dc.description.resumo???: Instrumentos endodônticos de NiTi foram analisados por meio de um Microscópio Eletrônico de Varredura (MEV) acoplado a um Espectômetro de Raio X por Energia Dispersiva (EDAX), antes e após o uso, com o objetivo de avaliar a presença de defeitos, deformações e analisar a sua composição química. Para isso, trinta instrumentos foram separados em 3 grupos, 10 limas ProTaper Next®X1(PNX1), 10 limas ProTaper Next®X2 (PNX2) e 10 limas WoveOne® (WO), as quais foram Elétromicrografados com aumento de 250 vezes, na região da ponta, 2mm e a 4mm da ponta. Os instrumentos foram utilizados no preparo de 60 blocos de canais simulados fabricados em resina poliéster. Inicialmente foi realizado o cateterismo com lima tipo K #10 e no comprimento de trabalho (CT), seguido pela instrumentação de acordo com cada grupo. Grupo 1: 10 blocos de canais simulados foram instrumentados com o sistema ProTaper Next®, utilizando a lima X1 para instrumentação do terço cervical e médio e a X2 para o terço apical. O grupo 2: 10 blocos foram instrumentados com a lima Primary 25.08 do sistema WaveOne® de acordo com as recomendações do fabricante. Os instrumentos foram utilizados primeiramente 1 vez e depois reutilizados 2 vezes, sempre em canais simulados novos. A limas foram lavadas em cuba ultrassônica e submetidas a nova análise microscópica pelo MEV e EDAX. Em seguida, as elétromicrografias foram tomadas na ponta do instrumento, a 2mm e a 4mm da ponta, com aumento de 250X. Para estabelecimento dos scores foram observados a presença de bordas irregulares, ranhuras, microcavidades e rebarbas. Cada instrumento quando comparados entre si no mesmo comprimento durante os três tempos de utilização não apresentaram diferença estatística em relação ao aumento dos defeitos (p>0,05). Em relação aos escores, a análise estatística dos resultados evidenciou que somente as limas WO apresentaram maior número de defeitos e deformações no comprimento de 4mm, nos 3 tempos de avaliação do estudo (p< 0.05). Foi observado na análise dos elementos químicos que as limas PNX1 apresentaram perdas significativas de Ni quando comparada as médias antes do uso e após a terceira utilização (p<0,01); nas limas PNX2 e WO houve perda significativa de Ni nos três tempos do uso (p<0,01). Em relação ao Ti, nas limas PNX1 não houve perda significativa ao longo do uso (p>0,05), porém, nas limas PNX2 apresentou perda significativa entre antes e a primeira instrumentação e entre o primeiro e terceiro uso (p<0,01). Nas limas WO, houve perda significativa quando comparamos antes e após a primeira utilização e antes com o terceiro uso. Assim, o reuso demonstrou que os instrumentos apresentaram todos os defeitos e deformações em algum comprimento e momento da pesquisa porém não aumentaram conforme o uso. Ocorreu perda apenas de Ni nas limas ProTaper Next® X1 após o uso e nas limas ProTaper Next® X2 e WaveOne® houve perda de Ni e Ti após as 3 utilizações.
Abstract: Endodontic instruments NiTi were analyzed using a Scanning Electron Microscope (SEM) coupled to a Spectrometer X-ray by Energy Dispersive (EDAX), before and after use, in order to assess the presence of defects, deformations and analyze its chemical composition. To this end, thirty instruments were divided into 3 groups, 10 Protaper Next®X1 files (PNX1), 10 Protaper Next®X2 files (PNX2) and 10 WoveOne® files (WO), which were electromicrograph 250-fold increase in tip region, the tip of 2mm and 4mm. The instruments were used in the preparation of 60 simulated canals blocks made of polyester resin. Initially we performed the catheterization with K file # 10 and the length (CT), followed by instrumentation according to each group. Group 1: 10 blocks of simulated canals were instrumented with ProTaper NEXT® system using the file X1 to instrumentation of the cervical and middle third and X2 to the apical third. Group 2: 10 blocks were instrumented with the WaveOne® 25.08 Primary file system according to the manufacturer's recommendations. The instruments were first used one time and then reused 2 times, always in new simulated channels. The files were washed in ultrasonic tank and subjected to new microscopic analysis by SEM and EDAX. Then the elétromicrografias were taken at the tip of the instrument, the tip of 2mm and 4mm, with an increase of 250X. To establish the scores were observed the presence of jagged edges, grooves, wells and burrs. Each instrument when compared with each other in the same length over the three days of use showed no statistical difference in relation to the increase in defects (p> 0.05). Regarding the scores, statistical analysis of the results showed that only WO files showed a higher number of defects and deformations in the length of 4mm, the third time evaluation of the study (p <0.05). It has been observed in the analysis of the chemical elements that PNX1 files showed significant losses compared to the average Ni before use and after the third application (p <0.01); PNX2 the files and WO significant loss of Ni in the three days of use (p <0.01). Regarding Ti, PNX1 files in no significant loss during use (p> 0.05), but the files PNX2 showed significant loss between before and the first instrumentation and between the first and third use (p <0, 01). In WO files, a significant loss when compared before and after the first use and prior to the third use. Thus, reuse demonstrated that the instruments had all defects and deformations at some length and time of the study but not increased with use. Loss occurred only in ProTaper Ni NEXT® X1 files after use and the ProTaper files NEXT® X2 and WaveOne® was no loss of Ni and Ti after 3 uses.
Keywords: Endodontia
Instrumentos odontológicos
Microscopia
Endodontics
Dental instruments
Microscopy
???metadata.dc.subject.cnpq???: CIÊNCIAS DA SAÚDE: ODONTOLOGIA
Language: por
???metadata.dc.publisher.country???: Brasil
Publisher: Universidade Federal do Amazonas
???metadata.dc.publisher.initials???: UFAM
???metadata.dc.publisher.department???: Faculdade de Odontologia
???metadata.dc.publisher.program???: Programa de Pós-graduação em Odontologia
Citation: BASTOS, Mariana Barreto. Efeito do reuso sobre as características de superfície e da composição química de instrumentos de NiTi. 2016. 55 f. Dissertação ( Mestrado em Odontologia) - Universidade Federal do Amazonas, Manaus, 2016.
???metadata.dc.rights???: Acesso Aberto
URI: http://tede.ufam.edu.br/handle/tede/5023
Issue Date: 1-Mar-2016
Appears in Collections:Mestrado em Odontologia

Files in This Item:
File Description SizeFormat 
Dissertação - Mariana Mena Barreto Bastos.pdf12.21 MBAdobe PDFThumbnail

Download/Open Preview


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.